Tungsten carbide rods – Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers https://www.wolframcarbide.com Tungsten carbide rods | Tungsten carbide strips | Tungsten carbide buttons| Carbide inserts | Carbide tips | Carbide plate | Carbide blades | carbide sleeves Fri, 19 Jun 2026 13:17:33 +0000 en-US hourly 1 https://wordpress.org/?v=7.0 https://www.wolframcarbide.com/wp-content/uploads/2025/07/cropped-Bortome-logo-32x32.jpg Tungsten carbide rods – Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers https://www.wolframcarbide.com 32 32 Manufacturer of tungsten carbide rods with coolant holes K20 https://www.wolframcarbide.com/product/carbide-rods-with-coolant-holes/ Fri, 01 May 2026 06:09:00 +0000 https://www.wolframcarbide.com/?post_type=product&p=3848 Carbide rods with coolant holes.

Diameter from 2 mm to 50 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep tungsten carbide rods with coolant holes in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience.
  5. The carbide rods with coolant holes performance and service life are close to 90-97% of Guhringg, Boehleritt and Kennametall.

Manufacturer of tungsten carbide rods with coolant holes K20最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> Grades of tungsten carbide rods with coolant holes:
Grade ISO Grade WC
(%)		 Co
(%)		 Grain Size
(μm)		 Hardness
（HRA）		 Density
（g/cm³）		 TRS
（N/mm²）
BU06 K05 – K10 94 6 0.5 94 14.75 3600
BU09 K20-K30 91 9 0.4 94 14.4 3800
YG10X K20 – K30 90 10 0.8 91.5 14.35 3600
BT15 K20 – K30 90 10 0.7 92.2 14.35 3900
BT20 K20 – K30 90 10 0.6 92.3 14.4 4000
BT25 K30 – K40 88 12 0.6 92.5 14.1 4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05 4200

Grade BU06: This grade is suitable for machining aluminum magnesium alloy, graphite, plastic, wood and composite material, etc.

Grade BU09: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 65.

Grade YG10X: This grade is suitable for machining materials such as common steel, non-ferrous metals, and cast iron, etc. It can process materials with hardness up to HRC 45. This grade is is popular in the Asian market, especially the Indian market.

Grade BT15: This grade is suitable for machining common steel, cast iron, stainless steel, heat-resistant steel, chilled hardened steel, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.  This grade is popular in the European market, especially in German market. Other markets, such as the USA, Canada, Korea, etc.

Grade BT20: This grade is suitable for machining stainless steel, heat-resistant steel, chilled hardened steel, cast iron, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.

Grade BT25: This grade is suitable for machining alloy steel, titanium alloy, chilled hardened steel cast iron, aluminum alloy, etc. It can process materials with hardness up to HRC 60.

Grade BT25UF: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 62.

Sizes of tungsten carbide rods with coolant holes:

 

Helical carbide rods sizes

Type D L
(Tol./0,+4)		 d TK a Pitch
φ(mm) Tol(mm) d(mm) Tol(mm) TK(mm) Tol(mm) P(mm) Tol(mm)
Bφ6×2φ0.7x26x330H30° 6 +0.7,+1.3 330 0.70 ±0.10 2.60 0,-0.4 0.15 32.65 +0.67,-0.65
Bφ7×2φ1.0×3.7x330H30° 7 +0.7,+1.3  330 1.00 ±0.15 3.70 0,-0.4 0.15 38.09 +0.78,-0.76
Bφ8×2φ1.0×4.0x330H30° 8 +0.7,+1.3  330 1.00 ±0.15 4.00 0,-0.4 0.15 43.53 +0.89,-0.86
Bφ9×2φ1.4×4.8x330H30° 9 +0.7,+1.3 330 1.40 ±0.15 4.80 0,-0.6 0.20 48.97 +1.00,-0.97
Bφ10×2φ1.4×4.8x330H30° 10 +0.7,+1.3 330 1.40 ±0.15 4.80 0,-0.6 0.20 54.41 +1.11.-1.08
Bφ11×2φ1.4×5.3x330H30° 11 +0.7,+1.4  330 1.40 ±0.15 5.30 0,-0.8 0.30 59.86 +1.22,-1.19
Bφ12×2φ1.4×6.25x330H30° 12 +0.7,+1.4 330 1.40 ±0.15 6.25 0,-0.8 0.30 65.3 +1.34,-1.30
Bφ13×2φ1.75×6.5x330H30° 13 +0.7,+1.4 330 1.75 ±0.20 6.50 0,-0.8 0.37 70.74 +1.45,-1.40
Bφ14×2φ1.75×7.1x330H30° 14 +0.7,+1.5  330 1.75 ±0.20 7.10 0,-0.8 0.40 76.18 +1.56,-1.51
Bφ15×2φ1.75×7.7x330H30° 15 +0.7,+1.5  330 1.75 ±0.20 7.70 0,-0.8 0.40 81.62 +1.67,-1.62
Bφ16×2φ1.75×8.3x330H30° 16 +0.7,+1.6  330 1.75 ±0.20 8.30 0,-0.8 0.40 87.06 +1.78,-1.83
Bφ17×2φ1.75×8.9x330H30° 17 +0.7,+1.6  330 1.75 ±0.20 8.90 0,-0.8 0.45 92.5 +1.89,-1.84
Bφ18×2φ2.3×9.55x330H30° 18 +0.7,+1.7  330 2.30 ±0.25 9.55 0,-0.8 0.50 97.95 +2.00,-1.94
Bφ19×2φ2.3×10.1x330H30° 19 +0.7,+1.7 330 2.30 ±0.25 10.10 0,-0.8 0.50 103.39 +2.12-2.05
Bφ20×2φ2.5×10.4x330H30° 20 +0.7,+1.7 330 2.50 ±0.25 10.40 0,-10 0.50 108.83 +2.23.-2.16
New sizes of carbide rods with coolant holes for your reference:
Φ4*330-Φ0.4*1-30° Φ4*330-Φ0.4*1-40°
φ6*330*2φ0.7*2.6-30° φ6*330*2φ0.7*2.6-40°
φ8*330*2φ1.0*4.0-30° φ8*330*2φ1.0*4.0-40°
φ10*330*2φ1.4*4.8-30° φ10*330*2φ1.4*4.8-40°
φ12*330*2φ1.4*6.25-30° φ12*330*2φ1.4*6.25-40°
φ14*330*2φ1.75*7.1-30° φ14*330*2φ1.75*7.1-40°
φ16*330*2φ1.75*8.3-30° φ16*330*2φ1.75*8.3-40°
φ18*330*2φ2.0*9.55-30° φ18*330*2φ2.0*9.55-40°
φ20*330*2φ2.0*10.4-30° φ20*330*2φ2.0*10.4-40°
Φ21*330-Φ2*10.5-30° Φ21*330-Φ2*10.5-40°
Φ22*330-Φ2*11.1-30° Φ22*330-Φ2*11.1-40°
Φ23*330-Φ2*11.7-30° Φ23*330-Φ2*11.7-40°
Φ24*330-Φ2*12.3-30° Φ24*330-Φ2*12.3-40°
Φ25*330-Φ2.5*12.3-30° Φ25*330-Φ2.5*12.3-40°
Φ26*330-Φ2*13.3-30° Φ26*330-Φ2*13.3-40°
Φ28*330-Φ2.5*14.2-30° Φ28*330-Φ2.5*14.2-40°
Φ30*330-Φ2.5*15.4-30° Φ30*330-Φ2.5*15.4-40°
Φ32*330-Φ3*16.6-30° Φ32*330-Φ3*16.6-40°
carbide rods with coolant holes drawing
Type D L
(Tol./0,+4)		 d a
φ(mm) Tol. (mm) d(mm) Tol. (mm)
Bφ6xφ1×330 6 +0.30/+0.60 330 1 ±0.15 0.15
Bφ7xφ1×330 7 +0.30/+0.60 330 1 ±0.15 0.15
Bφ7xφ1×330 8 +0.30/+0.60 330 1 ±0.15 0.15
Bφ9xφ1.4×330 9 +0.30/+0.70 330 1.4 ±0.15 0.2
Bφ10xφ1.4×330 10 +0.30/+0.70 330 1.4 ±0.15 0.2
Bφ11xφ1.4×330 11 +0.30/+0.70 330 1.4 ±0.15 0.3
Bφ12xφ1.75×330 12 +0.30/+0.80 330 1.75 ±0.15 0.3
Bφ13xφ1.75×330 13 +0.30/+0.80 330 1.75 ±0.15 0.4
Bφ14xφ1.75×330 14 +0.30/+0.80 330 1.75 ±0.15 0.4
Bφ15xφ2×330 15 +0.40/+0.80 330 2 ±0.20 0.4
Bφ16xφ2×330 16 +0.40/+0.80 330 2 ±0.20 0.4
Bφ17xφ2×330 17 +0.40/+0.80 330 2 ±0.20 0.5
Bφ18xφ2×330 18 +0.40/+0.80 330 2 ±0.20 0.5
Bφ19xφ2×330 19 +0.40/+0.80 330 2 ±0.20 0.5
Bφ20xφ2.5×330 20 +0.40/+0.80 330 2.5 ±0.25 0.5
Bφ22xφ2.5×330 22 +0.40/+0.80 330 2.5 ±0.25 0.5
Bφ24xφ2.5×330 24 +0.40/+0.80 330 3 ±0.25 0.5
Bφ25xφ2.5×330 25 +0.40/+0.80 330 3 ±0.25 0.5
Professional customized service available. We can strictly follow your drawings and technical requirements to tailor exclusive dimensions, meeting diverse application needs.

 

Details of tungsten carbide rods with coolant holes:

tungsten carbide rods with coolant holes

tungsten carbide rods with coolant holes

Please send us inquiries for quotations and free samples for testing:

Manufacturer of tungsten carbide rods with coolant holes K20最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High quality K10 K20 K30 tungsten carbide round bar suppliers https://www.wolframcarbide.com/product/tungsten-carbide-round-bar/ Sat, 13 Dec 2025 07:11:05 +0000 https://www.wolframcarbide.com/?post_type=product&p=3603 Tungsten carbide round bars.

Diameter from 2 mm to 50 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep carbide round bars in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience. The top ten largest carbide round bar manufacturers.
  5. The tungsten carbide round bar performance and service life are close to 95-100% of Guhringg, Cerztizitt, Boehleritt and Kennametall.

High quality K10 K20 K30 tungsten carbide round bar suppliers最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> 1. Tungsten carbide round bar grades：
Grade ISO Grade WC
(%)		 Co
(%)		 Grain Size
(μm)		 Hardness
（HRA）		 Density
（g/cm³）		 TRS
（N/mm²）
BU06 K05 – K10 94 6 0.5 94 14.75 3600
BU09 K20 – K30 91 9 0.4 94 14.4 3800
YG10X K20 – K30 90 10 0.8 91.5 14.35 3600
BT15 K20 – K30 90 10 0.7 92.2 14.35 3900
BT20 K20 – K30 90 10 0.6 92.3 14.4 4000
BT25 K30 – K40 88 12 0.6 92.5 14.1 4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05 4200

Grade BU06: This grade is suitable for machining aluminum magnesium alloy, graphite, plastic, wood and composite material, etc.

Grade BU09: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 65.

Grade YG10X: This grade is suitable for machining materials such as common steel, non-ferrous metals, and cast iron, etc. It can process materials with hardness up to HRC 45. This grade is is popular in the Asian market, especially the Indian market.

Grade BT15: This grade is suitable for machining common steel, cast iron, stainless steel, heat-resistant steel, chilled hardened steel, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.  This grade is popular in the European market, especially in German market. Other markets, such as the USA, Canada, Korea, etc.

Grade BT20: This grade is suitable for machining stainless steel, heat-resistant steel, chilled hardened steel, cast iron, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.

Grade BT25: This grade is suitable for machining alloy steel, titanium alloy, chilled hardened steel cast iron, aluminum alloy, etc. It can process materials with hardness up to HRC 60.

Grade BT25UF: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 62.

 

2. Tungsten carbide round bar sizes：

tungsten carbide round bar drawing

OD(MM) Length(MM)
0.2-60 10-330
3. Tungsten carbide round bars surface condition：

Sintered sand blasting surface:

tungsten carbide round bar

Ground and polished surface h5 and h6:

carbide round bar

Tungsten carbide round bars with coolant holes:

tungsten carbide round bars

Please send us inquiries for quotations and free samples for testing:

 

High quality K10 K20 K30 tungsten carbide round bar suppliers最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High performance K10 K20 K30 tungsten carbide bars stock https://www.wolframcarbide.com/product/tungsten-carbide-bars/ Sat, 13 Dec 2025 05:25:41 +0000 https://www.wolframcarbide.com/?post_type=product&p=3595 Tungsten carbide bars.

Diameter from 2 mm to 50 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep carbide bars in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience. The top ten largest carbide bar manufacturers.
  5. The tungsten carbide bars performance and service life are close to 95-100% of Guhringg, Cerztizitt, Boehleritt and Kennametall.

High performance K10 K20 K30 tungsten carbide bars stock最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> 1. Grades of tungsten carbide bars：
Grade ISO Grade WC
(%)		 Co
(%)		 Grain Size
(μm)		 Hardness
（HRA）		 Density
（g/cm³）		 TRS
（N/mm²）
BU06 K05 – K10 94 6 0.5 94 14.75 3600
BU09 K20 – K30 91 9 0.4 94 14.4 3800
YG10X K20 – K30 90 10 0.8 91.5 14.35 3600
BT15 K20 – K30 90 10 0.7 92.2 14.35 3900
BT20 K20 – K30 90 10 0.6 92.3 14.4 4000
BT25 K30 – K40 88 12 0.6 92.5 14.1 4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05 4200

Grade BU06: This grade is suitable for machining aluminum magnesium alloy, graphite, plastic, wood and composite material, etc.

Grade BU09: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 65.

Grade YG10X: This grade is suitable for machining materials such as common steel, non-ferrous metals, and cast iron, etc. It can process materials with hardness up to HRC 45. This grade is is popular in the Asian market, especially the Indian market.

Grade BT15: This grade is suitable for machining common steel, cast iron, stainless steel, heat-resistant steel, chilled hardened steel, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.  This grade is popular in the European market, especially in German market. Other markets, such as the USA, Canada, Korea, etc.

Grade BT20: This grade is suitable for machining stainless steel, heat-resistant steel, chilled hardened steel, cast iron, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.

Grade BT25: This grade is suitable for machining alloy steel, titanium alloy, chilled hardened steel cast iron, aluminum alloy, etc. It can process materials with hardness up to HRC 60.

Grade BT25UF: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 62.

 2. Sizes of tungsten carbide bars：

tungsten carbide bars drawing

OD(MM) Length(MM)
0.2-60 10-330
3. Tungsten carbide bars surface condition：

Sintered sand blasting surface:

tungsten carbide bars

Ground and polished surface h5 and h6:

carbide bars

Tungsten carbide bars with coolant holes:

tungsten carbide bars with coolant holes

Please send us inquiries for quotations and free samples for testing:

 

High performance K10 K20 K30 tungsten carbide bars stock最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> 0.2, 0.3, 0.5, 0.6, 0.8, 1MM tungsten carbide rods https://www.wolframcarbide.com/product/1mm-tungsten-carbide-rods/ Sun, 26 Oct 2025 08:24:57 +0000 https://www.wolframcarbide.com/?post_type=product&p=3527 Tungsten carbide rods specification.

Diameter 0.2mm, 0.3mm, 0.5mm, 0.6mm, 0.7mm, 0.8mm, 1mm, 1.2mm, 1.4mm, 1.5mm, 1.6mm, 1.8mm, 2.0mm, 2.3mm, 2.5mm, 2.8mm, 3.0mm.

Length from 10 mm to 330 mm.

Tolerance: Sintered and sand blasting, or ground h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep wolfram carbide rods in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience.
  5. The 1mm tungsten carbide rods performance and service life are close to 90-97% of Guhringg, Ceratizitt, Boehleritt and Kennametall.

0.2, 0.3, 0.5, 0.6, 0.8, 1MM tungsten carbide rods最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> 1MM tungsten carbide rods grades:
     Grade       ISO Grade  WC
(%)		    Co
  (%)		 Grain Size
      (μm)		 Hardness
（HRA）		    Density
  （g/cm³）		     TRS
   （N/mm²）
BU06 K05-K10 94 6 0.5 94    14.75        3600
YG10X K20 – K30 90 10 0.8 91.5 14.35       3600
BT15 K20 – K30 90 10 0.7 92.2 14.35       3900
BT20 K20 – K30 90 10 0.6 92.3 14.4     4000
BT25 K30 – K40 88 12 0.6 92.5 14.1      4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05     4200

Grade BU06: This grade is suitable for machining aluminum magnesium alloy, graphite, plastic material, wood and composite material, printed circuit board, tooth, etc.

Grade BU09: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 65.

Grade YG10X: This grade is suitable for machining materials such as common steel, non-ferrous metals, and cast iron, etc. It can process materials with hardness up to HRC 45. This grade is is popular in the Asian market, especially the Indian market.

Grade BT15: This grade is suitable for machining common steel, cast iron, stainless steel, heat-resistant steel, chilled hardened steel, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.  This grade is popular in the European market, especially in German market. Other markets, such as the USA, Canada, Korea, etc.

Grade BT20: This grade is suitable for machining stainless steel, heat-resistant steel, chilled hardened steel, cast iron, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.

Grade BT25: This grade is suitable for machining alloy steel, titanium alloy, chilled hardened steel cast iron, aluminum alloy, etc. It can process materials with hardness up to HRC 60.

Grade BT25UF: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 62.

1mm tungsten carbide rods details:

1mm tungsten carbide rods

1mm tungsten carbide rods manufacturer1.6mm tungsten carbide rods

 

Please send us inquiries for quotations and free samples for testing:

0.2, 0.3, 0.5, 0.6, 0.8, 1MM tungsten carbide rods最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High quality tungsten carbide preforms manufacturer https://www.wolframcarbide.com/product/tungsten-carbide-preforms-manufacturer/ Sat, 10 May 2025 06:09:41 +0000 https://www.wolframcarbide.com/?post_type=product&p=3101 Tungsten carbide preforms:

Diameter from 2 mm to 800 mm.

Thickness from 1 mm to 200mm.

Length from 10 mm to 2000 mm.

Accepting customized sizes.

Tolerance: h5 and h6 or sintered.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep tungsten carbide preforms in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. Custom shapes: Rods, plates, bushings, sleeves, seal rings, EDM blocks, can tooling, forming rolls, powder compacting, stamping, saw blades, dies, cutters, drill blanks,  oil field, slitter knives, bed knives, rotor knives, wear parts, punches, automotive, milling tool blanks, balls, seats, nozzles.
  5. Serving industries: Special cutting tools, Oil & Gas, Mold industry, Automotive, Mining, Manufacturing, Beverage & Aerosol, Housing, Medical, and Recycling.
  6. More than 40 years of manufacturing experience.
  7. The carbide preforms performance and service life are close to 95-100% of Guhringg, Boehleritt and Kennametall.

High quality tungsten carbide preforms manufacturer最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> Tungsten carbide preforms grade:
     Grade       ISO Grade  WC
(%)		    Co
  (%)		 Grain Size
      (μm)		 Hardness
（HRA）		    Density
  （g/cm³）		     TRS
   （N/mm²）
BU06 K05-K10 94 6 0.5 94    14.75        3600
YG10X K20 – K30 90 10 0.8 91.5 14.35       3600
BT15 K20 – K30 90 10 0.7 92.2 14.35       3900
BT20 K20 – K30 90 10 0.6 92.3 14.4     4000
BT25 K30 – K40 88 12 0.6 92.5 14.1      4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05     4200
Carbide preforms details:
tungsten carbide preforms

carbide preforms

tungsten carbide preforms manufacturer

 

Our experience:

With decades of expertise in non-standard hard alloy manufacturing, Bortome Carbide has established a state-of-the-art production line in China, specializing in precision-engineered carbide prefabricated parts.

Leveraging advanced CIP (Cold Isostatic Pressing) billet forming technology and a fully integrated production system, we offer flexible order policies with no minimum quantity requirements, coupled with customized solutions tailored to client-specific blueprints. Our capabilities are further enhanced by a partner network providing precision grinding services and global express delivery, ensuring rapid fulfillment of complex, geometrically challenging tool blank materials.

 

FAQ for tungsten carbide preforms:
Q1: What is a tungsten carbide preform? What is near-net-shape?

A: Tungsten carbide preform is semi-finished carbide blank pre-machined with complex profiles (steps, tapers, coolant holes, special contours) at pressed compact stage before sintering. Near-net-shape means the sintered part is extremely close to final dimension, drastically reducing post-sinter grinding & wire EDM cost.

 

Q2: What grades of tungsten carbide preforms do you offer?

A: We supply full series cemented carbide grades: BU06, BU09, YG10X, BT15, BT20, BT25UF, YG6, YG8, YG10, YG13, YG15, YG20, YN5, YN6, YN8, YN10, YN14,YN15,YN20, ultrafine/submicron grain carbide, as well as equivalent ISO grades WC-Co, WC-Ni alloy for corrosion resistance. Grades can be customized based on customer’s working conditions (cutting, stamping, mining, wear parts).

 

Q3: Can you make non-cobalt tungsten carbide preforms?

A: Yes. We produce WC-Ni, WC-Ni-Cr preforms for corrosive working environment where cobalt leaching is forbidden.

 

Q4: Can you make preforms with internal coolant holes?

A: Yes. We pre-drill straight /spiral coolant holes on green preforms, holes keep intact after sintering without secondary drilling, greatly save processing cost for drill & end mill manufacturers.

 

Q5: Can you make preforms with internal coolant holes?

A: Yes. We pre-drill straight /spiral coolant holes on green preforms, holes keep intact after sintering without secondary drilling, greatly save processing cost for drill & end mill manufacturers.

 

Q6: What complex shapes can your carbide preforms support?

A: Step shafts, T-shape blanks, special nozzles, gear preforms, micro drill blanks, eccentric parts, grooved preforms, custom irregular profiles according to customer’s drawings.

 

Q7: What is the standard dimensional tolerance of sintered carbide preforms?

A: Standard tolerance: ±0.1mm for general preforms. Tighter tolerance ±0.03~±0.05mm is available for precision series with extra HIP treatment. All preforms allow small finish grinding to reach final drawing tolerance.

 

Q8: What is your lead time?

A: In-stock items can be shipped within 2–3 days. New non-standard customized orders take 7–15 working days, subject to processing complexity.

 

Q9: What is your MOQ for custom carbide preforms?

A: Small trial order MOQ: 1 piece for new development.

 

Please send us inquiries for quotations and free samples for testing:

 

High quality tungsten carbide preforms manufacturer最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High-end stepped carbide T-slot cutter rod blanks manufacturers https://www.wolframcarbide.com/product/stepped-carbide-t-slot-cutter-rod-blanks/ Mon, 20 Jan 2025 05:54:00 +0000 https://www.wolframcarbide.com/?post_type=product&p=2817 Stepped tungsten carbide T-slot cutter rod blanks:

Diameter from 6 mm to 200 mm.

Thickness from 1 mm to 100mm.

Length from 10 mm to 500 mm.

Accepting customized sizes.

Tolerance: h5 and h6 or sintered.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep tungsten carbide rods in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience.
  5. The stepped carbide T-slot cutter rod blanks performance and service life are close to 95-100% of Guhringg, Boehleritt and Kennametall.

High-end stepped carbide T-slot cutter rod blanks manufacturers最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> Stepped carbide T-slot cutter rod blanks grade:
     Grade       ISO Grade  WC
(%)		    Co
  (%)		 Grain Size
      (μm)		 Hardness
（HRA）		    Density
  （g/cm³）		     TRS
   （N/mm²）
BU06 K05-K10 94 6 0.5 94    14.75        3600
YG10X K20 – K30 90 10 0.8 91.5 14.35       3600
BT15 K20 – K30 90 10 0.7 92.2 14.35       3900
BT20 K20 – K30 90 10 0.6 92.3 14.4     4000
BT25 K30 – K40 88 12 0.6 92.5 14.1      4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05     4200
Stepped tungsten carbide T-slot cutter rod blanks details:
Tungsten carbide T-slot cutter blanks

Cemented carbide T-slot router bit blanks

Wolfram carbide T-slot router bit blanks

Please send us inquiries for quotations and free samples for testing:

 

High-end stepped carbide T-slot cutter rod blanks manufacturers最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High performance solid carbide rods with competitive prices K10 K20 K30 https://www.wolframcarbide.com/product/solid-carbide-rods/ Thu, 26 Dec 2024 07:17:07 +0000 https://www.wolframcarbide.com/?post_type=product&p=2695 Solid carbide rods.

Diameter from 2 mm to 50 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep carbide rods in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience. The top ten largest solid carbide rod manufacturers.
  5. The solid carbide rods performance and service life are close to 95-100% of Guhringg, Cerztizitt, Boehleritt and Kennametall.

High performance solid carbide rods with competitive prices K10 K20 K30最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> 1. Solid carbide rods grades：
Grade ISO Grade WC
(%)		 Co
(%)		 Grain Size
(μm)		 Hardness
（HRA）		 Density
（g/cm³）		 TRS
（N/mm²）
BU06 K05 – K10 94 6 0.5 94 14.75 3600
BU09 K20 – K30 91 9 0.4 94 14.4 3800
YG10X K20 – K30 90 10 0.8 91.5 14.35 3600
BT15 K20 – K30 90 10 0.7 92.2 14.35 3900
BT20 K20 – K30 90 10 0.6 92.3 14.4 4000
BT25 K30 – K40 88 12 0.6 92.5 14.1 4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05 4200

Grade BU06: This grade is suitable for machining aluminum magnesium alloy, graphite, plastic, wood and composite material, etc.

Grade BU09: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 65.

Grade YG10X: This grade is suitable for machining materials such as common steel, non-ferrous metals, and cast iron, etc. It can process materials with hardness up to HRC 45. This grade is is popular in the Asian market, especially the Indian market.

Grade BT15: This grade is suitable for machining common steel, cast iron, stainless steel, heat-resistant steel, chilled hardened steel, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.  This grade is popular in the European market, especially in German market. Other markets, such as the USA, Canada, Korea, etc.

Grade BT20: This grade is suitable for machining stainless steel, heat-resistant steel, chilled hardened steel, cast iron, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.

Grade BT25: This grade is suitable for machining alloy steel, titanium alloy, chilled hardened steel cast iron, aluminum alloy, etc. It can process materials with hardness up to HRC 60.

Grade BT25UF: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 62.

   2. Solid carbide rods sizes：

 

整体硬质合金棒材尺寸

OD(MM) Length(MM)
1-50 10-330
3. Solid carbide rod surface condition：

Sintered sand blasting surface:

整体硬质合金棒

 

Solid carbide rod

 

Ground and polished surface h5 and h6:

solid carbide rods supplier

 

Please send us inquiries for quotations and free samples for testing:

 

High performance solid carbide rods with competitive prices K10 K20 K30最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High-end and good quality tungsten steel rods with 3 helical coolant holes https://www.wolframcarbide.com/product/tungsten-steel-rods/ Tue, 17 Dec 2024 09:46:25 +0000 https://www.wolframcarbide.com/?post_type=product&p=2613 Tungsten steel rods with 3 helical coolant holes.

Diameter from 3 mm to 32 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep tungsten steel rods in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience.
  5. The tungsten steel rods performance and service life are close to 90-97% of Guhringg, Boehlerittand Kennametalt.

High-end and good quality tungsten steel rods with 3 helical coolant holes最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> Tungsten steel rod grade:
     Grade       ISO Grade  WC
(%)		    Co
  (%)		 Grain Size
      (μm)		 Hardness
（HRA）		    Density
  （g/cm³）		     TRS
   （N/mm²）
BU06 K05-K10 94 6 0.5 94    14.75        3600
YG10X K20 – K30 90 10 0.8 91.5 14.35       3600
BT15 K20 – K30 90 10 0.7 92.2 14.35       3900
BT20 K20 – K30 90 10 0.6 92.3 14.4     4000
BT25 K30 – K40 88 12 0.6 92.5 14.1      4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05     4200

 

Tungsten steel rod details:

tungsten steel rod

 

tungsten steel rods

 

Please send us inquiries for quotations and free samples for testing:

High-end and good quality tungsten steel rods with 3 helical coolant holes最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> Carbide blanks with 1 central straight coolant hole https://www.wolframcarbide.com/product/carbide-blanks-with-one-central-straight-coolant-hole/ Sun, 01 Dec 2024 03:41:51 +0000 https://www.wolframcarbide.com/?post_type=product&p=2534 Carbide blanks with one central straight coolant hole.

Diameter from 6mm to 25 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 ,h6 and sintered.

  1. Raw material selection: High quality carbide blank powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep tungsten carbide rods in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience.
  5. The carbide carbide blanks performance and service life are close to 90-97% of Guhringg, Boehleritt and Kennametall.

Carbide blanks with 1 central straight coolant hole最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> 1. Carbide blanks grade:

     Grade       ISO Grade  WC
(%)		    Co
  (%)		 Grain Size
      (μm)		 Hardness
（HRA）		    Density
  （g/cm³）		     TRS
   （N/mm²）
BU06 K05-K10 94 6 0.5 94    14.75        3600
YG10X K20 – K30 90 10 0.8 91.5 14.35       3600
BT15 K20 – K30 90 10 0.7 92.2 14.35       3900
BT20 K20 – K30 90 10 0.6 92.3 14.4     4000
BT25 K30 – K40 88 12 0.6 92.5 14.1      4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05     4200

   2. Carbide blanks sizes:

carbide blanks

 

Type

 D         L
 (Tol./0,+4)		 d a
φ(mm) Tol. (mm) d(mm) Tol. (mm)
Bφ6xφ1×330 6 +0.30/+0.60 330 1 ±0.15 0.15
Bφ7xφ1×330 7 +0.30/+0.60 330 1 ±0.15 0.15
Bφ7xφ1×330 8 +0.30/+0.60 330 1 ±0.15 0.15
Bφ9xφ1.4×330 9 +0.30/+0.70 330 1.4 ±0.15 0.2
Bφ10xφ1.4×330 10 +0.30/+0.70 330 1.4 ±0.15 0.2
Bφ11xφ1.4×330 11 +0.30/+0.70 330 1.4 ±0.15 0.3
Bφ12xφ1.75×330 12 +0.30/+0.80 330 1.75 ±0.15 0.3
Bφ13xφ1.75×330 13 +0.30/+0.80 330 1.75 ±0.15 0.4
Bφ14xφ1.75×330 14 +0.30/+0.80 330 1.75 ±0.15 0.4
Bφ15xφ2×330 15 +0.40/+0.80 330 2 ±0.20 0.4
Bφ16xφ2×330 16 +0.40/+0.80 330 2 ±0.20 0.4
Bφ17xφ2×330 17 +0.40/+0.80 330 2 ±0.20 0.5
Bφ18xφ2×330 18 +0.40/+0.80 330 2 ±0.20 0.5
Bφ19xφ2×330 19 +0.40/+0.80 330 2 ±0.20 0.5
Bφ20xφ2.5×330 20 +0.40/+0.80 330 2.5 ±0.25 0.5
Bφ22xφ2.5×330 22 +0.40/+0.80 330 2.5 ±0.25 0.5
Bφ24xφ2.5×330 24 +0.40/+0.80 330 3 ±0.25 0.5
Bφ25xφ2.5×330 25 +0.40/+0.80 330 3 ±0.25 0.5

Please send us inquiries for quotations and free samples for testing:

Carbide blanks with 1 central straight coolant hole最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> High-end tungsten carbide rods with 2 helical coolant holes https://www.wolframcarbide.com/product/tungsten-carbide-rods-with-helical-coolant-holes/ Fri, 22 Nov 2024 12:20:23 +0000 https://www.wolframcarbide.com/?post_type=product&p=2488 Tungsten carbide rods with helical coolant holes.

Diameter from 2 mm to 50 mm.

Length from 10 mm to 330 mm.

Tolerance: h5 and h6.

  1. Raw material selection: High quality tungsten carbide powder is preferred. 100% virgin material.
  2. Imported German PVA sintering furnace. HIP sintering. Which can keep tungsten carbide rods in high density, High wear resistance, high-performance.
  3. Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
  4. More than 40 years of manufacturing experience.
  5. The tungsten carbide rods performance and service life are close to 90-97% of Guhringg, Boehleritt and Kennametall.

High-end tungsten carbide rods with 2 helical coolant holes最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]> Tungsten carbide rods with helical coolant holes grade:
     Grade       ISO Grade  WC
(%)		    Co
  (%)		 Grain Size
      (μm)		 Hardness
（HRA）		    Density
  （g/cm³）		     TRS
   （N/mm²）
BU06 K05-K10 94 6 0.5 94    14.75        3600
YG10X K20 – K30 90 10 0.8 91.5 14.35       3600
BT15 K20 – K30 90 10 0.7 92.2 14.35       3900
BT20 K20 – K30 90 10 0.6 92.3 14.4     4000
BT25 K30 – K40 88 12 0.6 92.5 14.1      4000
BT25UF K30 – K40 88 12 0.4 92.8 14.05     4200

 

Tungsten carbide rods with helical coolant hole sizes:

 

Helical carbide rods sizes

Type D L
(Tol./0,+4)		 d TK a Pitch
φ(mm) Tol(mm) d(mm) Tol(mm) TK(mm) Tol(mm) P(mm) Tol(mm)
Bφ6×2φ0.7×2.6x330H30° 6 +0.7,+1.3 330 0.70 ±0.10 2.60 0,-0.4 0.15 32.65 +0.67,-0.65
Bφ7×2φ1.0×3.7x330H30° 7 +0.7,+1.3  330 1.00 ±0.15 3.70 0,-0.4 0.15 38.09 +0.78,-0.76
Bφ8×2φ1.0×4.0x330H30° 8 +0.7,+1.3  330 1.00 ±0.15 4.00 0,-0.4 0.15 43.53 +0.89,-0.86
Bφ9×2φ1.4×4.8x330H30° 9 +0.7,+1.3 330 1.40 ±0.15 4.80 0,-0.6 0.20 48.97 +1.00,-0.97
Bφ10×2φ1.4×4.8x330H30° 10 +0.7,+1.3 330 1.40 ±0.15 4.80 0,-0.6 0.20 54.41 +1.11.-1.08
Bφ11×2φ1.4×5.3x330H30° 11 +0.7,+1.4  330 1.40 ±0.15 5.30 0,-0.8 0.30 59.86 +1.22,-1.19
Bφ12×2φ1.4×6.25x330H30° 12 +0.7,+1.4 330 1.40 ±0.15 6.25 0,-0.8 0.30 65.3 +1.34,-1.30
Bφ13×2φ1.75×6.5x330H30° 13 +0.7,+1.4 330 1.75 ±0.20 6.50 0,-0.8 0.37 70.74 +1.45,-1.40
Bφ14×2φ1.75×7.1x330H30° 14 +0.7,+1.5  330 1.75 ±0.20 7.10 0,-0.8 0.40 76.18 +1.56,-1.51
Bφ15×2φ1.75×7.7x330H30° 15 +0.7,+1.5  330 1.75 ±0.20 7.70 0,-0.8 0.40 81.62 +1.67,-1.62
Bφ16×2φ1.75×8.3x330H30° 16 +0.7,+1.6  330 1.75 ±0.20 8.30 0,-0.8 0.40 87.06 +1.78,-1.83
Bφ17×2φ1.75×8.9x330H30° 17 +0.7,+1.6  330 1.75 ±0.20 8.90 0,-0.8 0.45 92.5 +1.89,-1.84
Bφ18×2φ2.3x955x330H30° 18 +0.7,+1.7  330 2.30 ±0.25 9.55 0,-0.8 0.50 97.95 +2.00,-1.94
Bφ19×2φ2.3×10.1x330H30° 19 +0.7,+1.7 330 2.30 ±0.25 10.10 0,-0.8 0.50 103.39 +2.12-2.05
Bφ20×2φ2.5×10.4x330H30° 20 +0.7,+1.7 330 2.50 ±0.25 10.40 0,-10 0.50 108.83 +2.23.-2.16
New sizes for your reference:
Φ4*330-Φ0.4*1-30° Φ4*330-Φ0.4*1-40°
φ6*330*2φ0.7*2.6-30° φ6*330*2φ0.7*2.6-40°
φ8*330*2φ1.0*4.0-30° φ8*330*2φ1.0*4.0-40°
φ10*330*2φ1.4*4.8-30° φ10*330*2φ1.4*4.8-40°
φ12*330*2φ1.4*6.25-30° φ12*330*2φ1.4*6.25-40°
φ14*330*2φ1.75*7.1-30° φ14*330*2φ1.75*7.1-40°
φ16*330*2φ1.75*8.3-30° φ16*330*2φ1.75*8.3-40°
φ18*330*2φ2.0*9.55-30° φ18*330*2φ2.0*9.55-40°
φ20*330*2φ2.0*10.4-30° φ20*330*2φ2.0*10.4-40°
Φ21*330-Φ2*10.5-30° Φ21*330-Φ2*10.5-40°
Φ22*330-Φ2*11.1-30° Φ22*330-Φ2*11.1-40°
Φ23*330-Φ2*11.7-30° Φ23*330-Φ2*11.7-40°
Φ24*330-Φ2*12.3-30° Φ24*330-Φ2*12.3-40°
Φ25*330-Φ2.5*12.3-30° Φ25*330-Φ2.5*12.3-40°
Φ26*330-Φ2*13.3-30° Φ26*330-Φ2*13.3-40°
Φ28*330-Φ2.5*14.2-30° Φ28*330-Φ2.5*14.2-40°
Φ30*330-Φ2.5*15.4-30° Φ30*330-Φ2.5*15.4-40°
Φ32*330-Φ3*16.6-30° Φ32*330-Φ3*16.6-40°

Please send us inquiries for quotations and free samples for testing:

High-end tungsten carbide rods with 2 helical coolant holes最先出现在Tungsten carbide, wolfram carbide, cemented carbide products, manufacturers。

]]>