High-end 330 MM wolfram carbide rod blanks with high quality

330 MM wolfram carbide rod blanks.

Diameter from 2 mm to 50 mm.

Length from 10 mm to 330 mm.

Tolerance: Sintered and sand blasting.

Raw material selection: High quality wolfram carbide powder is preferred. 100% virgin material.
Imported German PVA sintering furnace. HIP sintering. Which can keep wolfram carbide rods in high density, High wear resistance, high-performance.
Professional engineers and quality inspection teams ensure product process inspection and acceptance inspection to ensure stable product quality and prevent unqualified products from being shipped.
More than 40 years of manufacturing experience.
The wolfram carbide rods performance and service life are close to 90-97% of Guhringg, Ceratizitt, Boehleritt and Kennametall.

Wolfram carbide rod blanks grades:

Grade	ISO Grade	WC (%)	Co (%)	Grain Size (μm)	Hardness （HRA）	Density （g/cm³）	TRS （N/mm²）
BU06	K05-K10	94	6	0.5	94	14.75	3600
YG10X	K20 – K30	90	10	0.8	91.5	14.35	3600
BT15	K20 – K30	90	10	0.7	92.2	14.35	3900
BT20	K20 – K30	90	10	0.6	92.3	14.4	4000
BT25	K30 – K40	88	12	0.6	92.5	14.1	4000
BT25UF	K30 – K40	88	12	0.4	92.8	14.05	4200

Grade BU06: This grade is suitable for machining aluminum magnesium alloy, graphite, plastic material, wood and composite material, etc.

Grade BU09: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 65.

Grade YG10X: This grade is suitable for machining materials such as common steel, non-ferrous metals, and cast iron, etc. It can process materials with hardness up to HRC 45. This grade is is popular in the Asian market, especially the Indian market.

Grade BT15: This grade is suitable for machining common steel, cast iron, stainless steel, heat-resistant steel, chilled hardened steel, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55. This grade is popular in the European market, especially in German market. Other markets, such as the USA, Canada, Korea, etc.

Grade BT20: This grade is suitable for machining stainless steel, heat-resistant steel, chilled hardened steel, cast iron, nickel base alloy and titanium alloy, etc. It can process materials with hardness up to HRC 55.

Grade BT25: This grade is suitable for machining alloy steel, titanium alloy, chilled hardened steel cast iron, aluminum alloy, etc. It can process materials with hardness up to HRC 60.

Grade BT25UF: This grade is suitable for machining alloy steel, stainless steel, aluminum alloy, chilled hardened steel and titanium alloy, etc. It can process materials with hardness up to HRC 62.